Technical Specifications
- Build Speed: 2-4 layers per minute
- Build Size: 254 x 356 x 203 mm
- For larger prototypes we can snap fit several sections together to form any sized prototype that is required.
- Layer Thickness: User selectable at the time of printing; 0.089-0.10 mm
- Material: High performance composite
- Resolution: 600 x 540 dpi in full colour.
- High performance composite material can be used to make strong, high-definition parts and is the material of choice for printing coloured parts.
- 3D Prototyping's printing materials meet many applications and business needs.
- 3D Prototyping parts can be sanded, drilled, tapped, painted and electroplated, further expanding the options available for finished part characteristics.
|
|
English | Metric |
| Tensile Strength |
2,800 psi |
19.29 Mpa |
| Tensile Modulus | 130,000 psi |
827 Mpa |
| Flexural Strength | 3,900 psi |
28 Mpa |
| Flexural Modulus | 120,000 psi |
827 Mpa |
| Impact Strength (Notched Izod) | 0.60 ft-lbs/in |
32 J/m |
| Impact Strength (Unnotched) |
23.00 ft-lbs/in |
1,228 J/m |
| Hardness (Shore D) |
62 (D) |
|
| Elongation |
< 10% |
|
- Measured points 1,400,000 points in 1 second
- Measurment time 1 second
- Measuring area (Min) 175 x 140mm (squared)
- Measuring area (Max) 2000 x 1600mm (squared)
- Cloud point spacing 0.12 - 1.4mm
- Stand off 730 -2000mm
Suitable files that can be exported in are STL, IGES, TXT, STEP ASCI and parasolid XT.
- SLA process is highly accurate and is suitable for fine detailed parts
- SLA process is excellent for light function testing and snap fitting of mating parts.
|
Material |
TSR-821 |
|
Tensile strength (Mpa) |
49 |
|
Elongation (%) |
13-15 |
|
Tensile Modulus (Mpa) |
1,800 |
|
Flexural Strength (Mpa) |
70 |
|
Flexural Modulus (Mpa) |
2,225 |
|
Impact strength (notched) |
48-49 |
|
Surface Hardness ( Shore D) |
82-85 |
|
Appearance |
Pale white |